Habka diyaarinta ee xabagta polyamide

Diyaarinta Dimeric Linoleic Acid: Linoleic acid, dhoobo, lithium carbonate, iyo biyo ayaa lagu daray reactor waxaana lagu walaaqay cadaadiska 0.8-1.2 MPa. Heerkulka ayaa kor loo qaaday ilaa 230 digrii wuxuuna ka falceliyay 5 saacadood. Isku darka ayaa markaa la qaboojiyey ilaa 100 darajo, iyo 1.92 g oo ah phosphoric acid xal aqueous ayaa lagu daray. Cadaadiska ayaa markaa hoos loo dhigay 0.3-0.5 MPa, heerkulkuna wuxuu kor u kacay 150 darajo 1 saac. Ugu dambeyntii, heerkulka ayaa hoos loo dhigay ilaa 100 darajo , isku dar ah ayaa la sifeeyay inta kulul si meesha looga saaro kicinta. Asiidhyada dufanka leh ee aan dheregsanayn ee aan polymerka lahayn ayaa markaas lagu soo daadiyey faakuum sare (6.7-10.7 Pa) at 220–225 darajo si loo helo {{20}nadiifinta dimerized linoleic acid sare.

Diyaarinta Polyamide Hot Melt Adhesive: Ilaalinta nitrogen, isku dhafka ethylenediamine iyo hexamethylenediamine ayaa si tartiib tartiib ah loogu daray iyadoo la walaaqayo lana kululeynayo isku dar ah 130 digrii. Halkaa marka ay marayso, heerkulka waxaa lagu xakameynayaa 140-150 digrii. Ka dib marka lagu daro dhamaystirka, heerkulka ayaa kor loogu qaadayaa 205-220 darajo iyo falcelintu way sii socotaa ilaa maadada biyaha ee badeecaddu ay u soo dhowaanayso qiimaha aragtida. Kadibna, cadaadiska waa la dhimay, falcelinta ayaa sii socota saacad kale 1.3-2.7 kPa iyo 220-230 digrii. Ugu dambeyntii, muunad ayaa la qaadayaa si loo go'aamiyo qiimaha aminiga. Haddii ay la kulanto tusmada (qiyaastii 10), badeecada waa la qaboojin karaa oo la sii dayn karaa. Meesha jilicsan ee xabagta dhalaalka kulul way kala duwan tahay iyadoo ku xiran qadarka dilinoleic acid, sebacic acid, ethylenediamine, iyo hexamethylenediamine ee la isticmaalo.